IR analysis of borate glasses containing three alkali oxides
L. Balachandera, G. Ramadevudub,*, Md. Shareefuddina, R. Sayannac, Y.C. Venudharc
ABSTRACT: FTIR investigations on borate glasses containing three alkali oxides, x Li2O·x Na2O·x K2O·(50−3x) PbO·50B2O3 (x=8, 10, 12, 14, and 16 mol%), 10Li2O·10Na2O·10K2O·y PbO·(70−y) B2O3 (y=25, 30, 35, 40, and 50 mol%), and x Li2O·x Na2O·x K2O·(50−3x) Bi2O3·50B2O3 (x=8, 10, 12, 14, and 16 mol%) are reported. The present glasses contain mainly BO3 and BO4 structural units. The presence of fingerprints of both BiO3 and BiO6 structural units in bismuth alkali borate glasses was confirmed. The presence of varied types like di, tetra, penta, and ortho borate groups are confirmed in the glass matrix. Glasses with low PbO content contained more BO3 units than BO4 units.
Download PDF
67 Downloads 1467 Views
a |
Department of Physics, Nizam College (Autonomous), Osmania University, Hyderabad 500 001, India |
b |
Department of Physics, Vasavi College of Engineering, Ibrahimbagh, Hyderabad 31, India |
c |
Department of Physics, Osmania University, Hyderabad 500 007, India |
* Corresponding author, E-mail: dr.ramdev@gmail.com
Received 4 Sep 2012, Accepted 28 Dec 2012
|